Bitumen Products - Catagorized by Usage

you can click on product that you like to see full specification

Oxidized bitumen

Coating Bitumen

Oxidized bitumen

Oxidized Bitumen or Blown bitumen grades are produced by passing air through the penetration grades. This process gives the bitumen more rubbery properties than its original formula and they are simply harder bitumen. Hard bitumen under controlled temperature conditions is widely used as an anti-slip layer compound in the piling industry, for the manufacture of roofing felts, the roofing and waterproofing industries, for sound dampening felts and under carriage sealant in the automotive industry, electric cable joint protection, joint filling compound, sealant compound and many others. Also used in sealing saw cuts and joints where expected movements are minimum. It is also used in the manufacturing of bituminous marine mastic for the oil & gas pipeline joints.

The most popular grades are; grades 95/25, 85/25, 90/40, and 115/15. We are also capable of producing other grades of Oxidized bitumen upon request by our customers. Oxidized Bitumen high softening temperatures qualify them as the excellent sealant for prevention from bleeding in high-temperature applications. Blown Grade Bitumen shall be broken up into small pieces (for the blown grade in molded cake form) and heated slowly to the application temperature of 220ºC to 230ºC. Oxidized Bitumen is predominantly used in the piling industry as an anti-slip compound for the manufacture of undercarriage sealants in the automobile industry. It is also used as a sealant compound, as a joint filling compound apart from being used in the manufacture of roofing felts and sound dampening felts. Further, Oxidized Bitumen is used in the manufacture of bituminous marine mastic, which is required for the oil and gas pipeline joints. This Oxidized Bitumen is available in different grades like 95/25, 85/25, 75/25, 90/40 and 115/15. Oxidized is also capable of producing other grades of Oxidized Bitumen according to the specifications of individual clients

Specifications

Specification of oxidized bitumen 150/5

Analysis oxidized bitumen 150/5

Bitumen 150/5	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	4/6
Softening point °c	ASTM D36	°C	145/155
Ductility @25 °c	ASTM D113	Cm	1.5min
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized bitumen 115/15

Analysis oxidized bitumen 115/15

Bitumen 115/15	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	10/20
Softening point °c	ASTM D36	°C	110/120
Ductility @25 °c	ASTM D113	Cm	1.5min
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Blown bitumen 105/35

Analysis bitumen 105/35

Bitumen 105/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	30/40
Softening point °c	ASTM D36	°C	100/110
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.

Oxidized asphalt 105/15

Analysis oxidized bitumen 105/15

Bitumen 105/15	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	10/20
Softening point °c	ASTM D36	°C	100/110
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized bitumen 95/25

Analysis bitumen 95/25

Bitumen 95/25	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	20/30
Softening point °c	ASTM D36	°C	90/100
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint °c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Blown asphalt 90/40

Analysis asphalt 90/40

Bitumen 90/40	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	35/45
Softening point °c	ASTM D36	°C	85/95
Ductility @25 °c	ASTM D113	Cm	5.5min
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

oxidized bitumen 90/15

Analysis bitumen 90/15

Bitumen 90/15	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	10/20
Softening point °c	ASTM D36	°C	85/95
Ductility @25 °c	ASTM D113	Cm	1.5min
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized asphalt 90/10

Analysis asphalt 90/10

Bitumen 90/10	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	5/15
Softening point °c	ASTM D36	°C	85/95
Ductility @25 °c	ASTM D113	Cm	1.5min
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Blown bitumen 85/40

Analysis bitumen 85/40

Bitumen 85/40	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	35/40
Softening point °c	ASTM D36	°C	80/90
Ductility @25 °c	ASTM D113	Cm	3
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	260 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99 min
Spot test	A.A.S.H.O.T 102	—	Negative

Blown asphalt 85/35

Analysis asphalt 85/35

Bitumen 85/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	30/40
Softening point °c	ASTM D36	°C	80/90
Ductility @25 °c	ASTM D113	Cm	1.5min
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flash point °c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Oxidized bitumen 85/25

Analysis bitumen 85/25

Bitumen 85/25	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	20/30
Softening point °c	ASTM D36	°C	80/90
Ductility @25 °c	ASTM D113	Cm	3 min
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T 102	—	Negative

Oxidized asphalt 75/35

Analysis asphalt 75/35

Bitumen 75/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	30/40
Softening point °c	ASTM D36	°C	70/80
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Blown asphalt 75/25

Analysis asphalt 75/25

Bitumen 75/25	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	20/30
Softening point °c	ASTM D36	°C	70/80
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Bitumen No. 10

Bitumen 10

Bitumen 10 is the type of hard grade building asphalt with penetration starting from #10 that is why it is famous asphalt number 10. Bitumen No.10 is available in bag and drum also the bulk tanker. This grade of asphalt building material is mostly using in eastern Asia market especially Taiwan and China also Philippine and Indonesia.

Uses of bitumen #10

1. For underground moisture, waterproofing works
2. For nuclear power engineering, pipeline engineering, bottom anticorrosion, asphalt production of the production
3. For waterproofing membrane, moisture-proof paper production, etc.
4. For Anti-corrosion paint and waterproof production
5. Used for road and bridge caulking use

Datasheet of bitumen number 10

Technical indicators	10
Penetration (25 ° C, 100 g, 5 s) / (0.1 mm)	10-26
The ductility (25 ° C, 5 cm / min) / cm is not less than	1.5
Softening point (ball method) / ℃ not less than	95
Solubility (trichloroethylene) /% is not less than	99.5
Evaporation loss (163 ° C, 5 h) /% no more than	1
After evaporation, the penetration ratio (25 ℃) /% is not less than	65
Flashpoint (open cup) / ℃ not less than	230
Brittle / ℃	report

Bitumen No. 30

Bitumen 30

Bitumen 30 is the soft grade of blown bitumen with softening point of 30+5 and softening point approx. 70C and it is available in bag and drum but in summer time it is risky to take it in the bag due to leakage of bitumen 30 inside of the container. Bitumen No.30 is producing by bitumen #60 and after heating up and lost 5% of total weight the first grade of oxidized bitumen is number 30.

Uses of bitumen #30

Datasheet of bitumen number 30

Technical indicators	30
Penetration (25 ° C, 100 g, 5 s) / (0.1 mm)	36-50
The ductility (25 ° C, 5 cm / min) / cm is not less than	3.5
Softening point (ball method) / ℃ not less than	60
Solubility (trichloroethylene) /% is not less than	99.5
Evaporation loss (163 ° C, 5 h) /% no more than	1
After evaporation, the penetration ratio (25 ℃) /% is not less than	65
Flashpoint (open cup) / ℃ not less than	230
Brittle / ℃	report

Bitumen No. 40

Bitumen 40

Bitumen 40 is made by the extract of bitumen #60 and it is the very soft grade of oxidized asphalt that should be packed in the steel drum. It is flexible bitumen while the softening point is high.This type of asphalt is useful to use in road construction to keep the asphalt stable against hot season and movement.

Uses of bitumen #40

Datasheet of bitumen number 30

Technical indicators	30
Penetration (25 ° C, 100 g, 5 s) / (0.1 mm)	10-35
The ductility (25 ° C, 5 cm / min) / cm is not less than	2.5
Softening point (ball method) / ℃ not less than	75
Solubility (trichloroethylene) /% is not less than	99.5
Evaporation loss (163 ° C, 5 h) /% no more than	1
After evaporation, the penetration ratio (25 ℃) /% is not less than	65
Flashpoint (open cup) / ℃ not less than	230
Brittle / ℃	report

Penetration Grade Bitumen

The penetration grade bitumen is refinery bitumen that is manufactured at different viscosities. The penetration test is carried out to characterize the bitumen, based on the hardness. Thus, it has the name penetration bitumen. The penetration bitumen grades range from 15 to 450 for road bitumen. But the most commonly used range is 25 to 200. This is acquired by controlling the test carried out i.e. the distillation process. The partial control of fluxing the residual bitumen with the oils can help in bringing the required hardness.

The BS EN 1426 and BS EN 1427 provides the penetration and softening point values for the respective grades, as from Table-1. This will help in identifying the equiviscosity and the hardness of the bitumen grade.

The grades are represented by the penetration values i.e. For example, 40/60 as a penetration value of 50 ± 10.

The BS EN 13303 also gives the measure of loss on heating with respective limits for all penetration bitumen grades. This measure is to ensure that there are no volatile components present.

So, no component whose loss will contribute to the setting and hardening of bitumen during its preparation or lay course is undergone. The BS EN 12592 provides the solubility values to ensure that there is less or no impurities in the bitumen material.

Specifications

Bitumen penetration grade 10/20

specification of bitumen penetration 10/20

Bitumen 10/20	Test method	Unit	Specification
Specific gravity @ 25°c	ASTM D70	Kg/cm3	1.01/1.06
Penetration @ 25°c	ASTM D5	Mm/10	10/20
Softening point °c	ASTM D36	°C	58/66
Ductility @25 °c	ASTM D113	Cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	0.2 max
Drop in penetration after heating %	ASTM D5-D6	%	20 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	wt %	99.5 max
Spot test	A.a.s.h.o.t102		Negative

Bitumen penetration grade 30/40

Specification of bitumen penetration grade 30/40

Bitumen 30/40	Test method	Unit	Specification
Specific gravity @ 25°c	ASTM D70	Kg/cm3	1.01/1.06
Penetration @ 25°c	ASTM D5	mm/10	30/40
Softening point °c	ASTM D36	°C	55/63
Ductility @25 °c	ASTM D113	cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	0.2 max
Drop in penetration after heating %	ASTM D5-D6	%	20 max
Flash point °c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	wt %	99.5 min
Spot test	A.A.S.H.O.T102		Negative

bitumen penetration grade 40/50

Specification of bitumen penetration grade 40/50

Bitumen 40/50	Test method	Unit	Specification
Specific gravity @ 25°c	ASTM D70	Kg/cm3	1.01/1.06
Penetration @ 25°c	ASTM D5	mm/10	40/50
Softening point °c	ASTM D36	°C	52/60
Ductility @25 °c	ASTM D113	cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	0.2 max
Drop in penetration after heating %	ASTM D5-D6	%	20 max
Flash point °c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	wt %	99.5 min
Spot test	A.A.S.H.O.T102		Negative

Bitumen penetration grade 60/70

Specification of bitumen penetration grade 60/70

Bitumen 60/70	Test method	Unit	Specification
Specific gravity @ 25°C	ASTM D70	Kg/cm3	1.01/1.06
Penetration @ 25°C	ASTM D5	mm/10	60/70
Softening point °C	ASTM D36	°C	49/56
Ductility @25 °C	ASTM D113	cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	0.2 max
Drop in penetration after heating %	ASTM D5-D6	%	20 max
Flashpoint °C	ASTM D92	°C	232 min
Solubility in Trichloroethylene	ASTM D2042	wt %	99 min
Spot test	A.A.S.H.O.T102		Negative

Bitumen penetration grade 80/100

Specification of bitumen penetration grade 80/100

Bitumen 80/100	Test method	Unit	Specification
Specific gravity @ 25°c	ASTM D70	Kg/cm3	1.01/1.06
Penetration @ 25°c	ASTM D5	mm/10	80/100
Softening point °c	ASTM D36	°C	42/50
Ductility @25 °c	ASTM D113	cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	0.2 max
Drop in penetration after heating %	ASTM D5-D6	%	20 max
Flash point °c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	wt %	99.5 min
Spot test	A.A.S.H.O.T102		Negative

Bitumen penetration grade 85/100

Specification of bitumen penetration grade 85/100

Bitumen 85/100	Test method	Unit	Specification
Specific gravity @ 25°c	ASTM D70	Kg/cm3	1.01/1.06
Penetration @ 25°c	ASTM D5	mm/10	85/100
Softening point °c	ASTM D36	°C	41/49
Ductility @25 °c	ASTM D113	Cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	0.2 max
Drop in penetration after heating %	ASTM D5-D6	%	20 max
Flash point c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	wt %	99.5 min
Spot test	A.A.S.H.O.T102		Negative

Bitumen penetration grade 120-150

Specification of bitumen penetration grade 120/150

Bitumen 120/150	Test method	Unit	Specification
Specific gravity @ 25°C	ASTM D70	Kg/m3	1000-1050
Penetration @ 25°C	ASTM D5	mm/10	120/150
Softening point °C	ASTM D36	°C	38 min
Ductility @25 °C	ASTM D113	Cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	0.5 max
Drop in penetration after heating %	ASTM D5-D6	%	20 max
Flashpoint °C	ASTM D92	°C	218 min
Solubility in Trichloroethylene	ASTM D2042	wt %	99 min
Spot test	—		Negative

bitumen penetration grade 200/300

Specification of bitumen penetration grade 200/300

Bitumen 200/300	Test method	Unit	Specification
Specific gravity @ 25°C	ASTM D70	Kg/m3	990-1040
Penetration @ 25°C	ASTM D5	mm/10	200/300
Softening point °C	ASTM D36	°C	32 min
Ductility @25 °C	ASTM D113	cm	100 min
Loss on heating(wt) %	ASTM D6	wt %	1 max
Drop in penetration after heating %	ASTM D5-D6	%	37 min
Flashpoint °C	ASTM D92	°C	177 min
Solubility in Trichloroethylene	ASTM D2042	wt %	99 min
Spot test	—		Negative

bitumen penetration grade 20/30

specification of bitumen penetration grade 20/30

Bitumen 20/30	Test method	Unit	Specification
Penetration @ 25°C	EN 1426	mm/10	20/30
Softening point °C	EN 1427	°C	53/65
Kinematic Viscosity @ 135⁰C	EN 12595	mm2/s	530 min
Flashpoint °C	EN 22592	°C	240 min
Solubility is CS2(wt) %	EN 12592	wt %	99 min

bitumen penetration grade 30/45

Specification of bitumen penetration grade 30/45

Bitumen 30/45	Test method	Unit	Specification
Penetration @ 25°C	IP 49	mm/10	30/45
Softening point °C	IP 58	°C	52/60
Kinematic Viscosity @ 135⁰C	IP 319	mm2/s	400 min
Flashpoint °C	IP 36	°C	240 min
Solubility is CS2(wt) %	IP 47	wt %	99 min

bitumen penetration grade 35/50

Specification of bitumen penetration grade 35/50

Bitumen 35/50	Test method	Unit	Specification
Penetration @ 25°c	IP 49	Mm/10	35/50
Softening point °c	IP 58	°C	50/58
Kinematic Viscosity @ 135⁰C	IP 370	mm2/s	400 min
Flash point°c	IP 36	°C	240 min
Solubility is CS2(wt) %	IP 47	wt %	99 min

bitumen penetration grade 40/60

Specification of bitumen penetration grade 40/60

Bitumen 40/60	Test method	Unit	Specification
Penetration @ 25°c	IP 49	mm/10	40/60
Softening point °c	IP 58	°C	48/56
Kinematic Viscosity @ 135⁰C	IP 370	mm2/s	325 min
Flash point°c	IP 36	°C	230 min
Solubility is CS2(wt) %	IP 47	wt %	99 min

bitumen penetration grade 50/70

Specification of bitumen penetration grade 50/70

Bitumen 50/70	Test method	Unit	Specification
Penetration @ 25°c	IP 49	mm/10	50/70
Softening point °c	IP 58	°C	46/54
Kinematic Viscosity @ 135⁰C	IP 370	mm2/s	295 min
Flash point°c	IP 36	°C	230 min
Solubility is CS2(wt) %	IP 47	wt %	99 min

Bitumen penetration grade 70/100

Specification of bitumen penetration grade 70/100

Bitumen 70/100	Test method	Unit	Specification
Penetration @ 25°C	IP 49	mm/10	70/100
Softening point °C	IP 58	°C	43/51
Kinematic Viscosity @ 135⁰C	IP 370	mm2/s	230 min
Flash point °C	IP 36	°C	225 min
Solubility is CS2(wt) %	IP 47	wt %	99 min

bitumen penetration grade 100/150

Specification of bitumen penetration grade 100/150

Bitumen 100/150	Test method	Unit	Specification
Penetration @ 25°c	IP 49	mm/10	100/150
Softening point °c	IP 58	°C	39/47
Kinematic Viscosity @ 135⁰C	IP 370	mm2/s	175 min
Flashpoint °c	IP 36	°C	230 min
Solubility is CS2(wt) %	IP 47	wt %	99 min

bitumen penetration grade 160/220

Specification of bitumen penetration grade 160/220

Bitumen 160/220	Test method	Unit	Specification
Penetration @ 25°c	IP 49	mm/10	160/220
Softening point °c	IP 58	°C	35/43
Kinematic Viscosity @ 135 °C	IP 370	mm2/s	135 min
Flashpoint °c	IP 36	°C	220 min
Solubility is CS2(wt) %	IP 47	wt %	99 min

Bitumen emulsion

Bitumen is the oldest known thermoplastic material in use today. Its usefulness and appeal derive from its simple thermoplastic property of being a thin liquid at high temperature and a virtual solid at ambient temperature. For the vast majority of applications, bitumen is used in the temperature range 140 to 230°C at a viscosity of around 200 cSt (20 Pa.$). For many applications, these conditions are both essential and desirable allowing rapid throughput from hot bulk bitumen delivery through to final use without any reheating. There are limitations to the coating film thickness that can be achieved using hot-applied techniques and for some applications, it is necessary to apply at a lower temperature and/or viscosity. The reasons may be a combination of the process requirements, the application techniques, safety and environmental requirements or final product properties. The two methods used mostly to modify bitumen properties are emulsification with water and dilution with hydrocarbon solvent enabling the bitumen to be applied cold, up to about 80°C for emulsions or up to about 150°C for cutbacks, depending on the dilution and solvent used.

Specifications

bitumen emulsion CSS-1

PropertyProperty	Min	Max	Test Method
Test on Emulsions
Viscosity, Saybolt Furol at 25 °C, SFS	20	100	ASTM D244
Storage stability test, 24-h, %	–	1	ASTM D6930
Particle charge test	positive		ASTM D244
Sieve test, %	–	0.1	ASTM D6933
Cement mixing test, %		2.0	ASTM D6935
Distillation:
Residue, %	57	–	ASTM D244
Tests on residue from distillation test:
Penetration, 25°C (77°F), 100 g, 5 s	100	250	ASTM D5
Ductility, 25°C (77°F), 5 cm/min, cm	40	–	ASTM D113
Solubility in trichloroethylene, %	97.5	–	ASTM D2042

Cationic Bitumen Emulsion CSS-1h

PropertyProperty MinMaxTest MethodTest on EmulsionsViscosity, Saybolt Furol at 25 °C, SFS20100ASTM D244Storage stability test, 24-h, %–1ASTM D6930Particle charge testpositiveASTM D244Sieve test, %–0.1ASTM D6933Cement mixing test, % 2.0ASTM D6935Distillation:Residue, %57–ASTM D244Tests on residue from distillation test:Penetration, 25°C (77°F), 100 g, 5 s4090ASTM D5Ductility, 25°C (77°F), 5 cm/min, cm40–ASTM D113Solubility in trichloroethylene, %97.5–ASTM D2042

Cationic Bitumen Emulsion CMS-2

PropertyminmaxTest methodTest on emulsionsViscosity, Saybolt Furol at 50 °C, SFS50450ASTM D244Storage stability test, 24-h, %–1ASTM D6930Coating ability and water resistance:Coating, dry aggregateGoodASTM D244Coating, after sprayingFairASTM D244Coating, wet aggregateFairASTM D244Coating, after sprayingFairASTM D244Particle charge testPositiveASTM D244Sieve test, %–0.1ASTM D6933Distillation:Oil distillate, by volume of emulsion, %–12ASTM D6997Residue, %65–ASTM D244Tests on residue from distillation test:Penetration, 25°C (77°F), 100 g, 5 s100250ASTM D5Ductility, 25°C (77°F), 5 cm/min, cm40–ASTM D113Solubility in trichloroethylene, %97.5– ASTM D2042

Cationic Bitumen Emulsion CMS-2h

PropertyminmaxTest methodTest on emulsionsViscosity, Saybolt Furol at 50 °C, SFS40450ASTM D244Storage stability test, 24-h, %–1ASTM D6930Coating ability and water resistance:Coating, dry aggregateGoodASTM D244Coating, after sprayingFairASTM D244Coating, wet aggregateFairASTM D244Coating, after sprayingFairASTM D244Particle charge testPositiveASTM D244Sieve test, %–0.1ASTM D6933Distillation:Oil distillate, by volume of emulsion, %–12ASTM D6997Residue, %65–ASTM D244Tests on residue from distillation test:Penetration, 25°C (77°F), 100 g, 5 s4090ASTM D5Ductility, 25°C (77°F), 5 cm/min, cm40–ASTM D113Solubility in trichloroethylene, %97.5– ASTM D2042

Cationic Bitumen Emulsion CRS-1

PropertyProperty	Min	Max	Test Method
Test on Emulsions
Viscosity, Saybolt Furol at 25 °C, SFS	20	100	ASTM D244
Storage stability test, 24-h, %	–	1	ASTM D6930
Demulsibility, 35 mL, 0.8 % dioctyl sodium sulfosuccinate, %	40	–	ASTM D6936
Coating ability and water resistance:
Particle charge test	Positive		ASTM D244
Sieve test, %	–	0.1	ASTM D6933
Distillation :
Oil distillate, by volume of emulsion, %	–	3	ASTM D6997
Residue, %	60	–	ASTM D244
Tests on residue from distillation test:
Penetration, 25°C (77°F), 100 g, 5 s	100	250	ASTM D5
Ductility, 25°C (77°F), 5 cm/min, cm	40	–	ASTM D113
Solubility in trichloroethylene, %	97.5	–	ASTM D2042

Cationic Bitumen Emulsion CRS-2

PropertyProperty MinMaxTest MethodTest on EmulsionsViscosity, Saybolt Furol at 25 °C, SFS100400ASTM D244Storage stability test, 24-h, %–1ASTM D6930Demulsibility, 35 mL, 0.8 % dioctyl sodium sulfosuccinate, %40–ASTM D6936Coating ability and water resistance:Particle charge testPositiveASTM D244Sieve test, %–0.1ASTM D6933Distillation : Oil distillate, by volume of emulsion, %–3ASTM D6997Residue, %65–ASTM D244Tests on residue from distillation test:Penetration, 25°C (77°F), 100 g, 5 s100250ASTM D5Ductility, 25°C (77°F), 5 cm/min, cm40–ASTM D113Solubility in trichloroethylene, %97.5–ASTM D2042

Iran Cationc Bitumen Emulsion K1-40 Manufacturer

Technical Data Sheet of Cationic Bitumen Emulsion K1-40

No	Property	Test Method	Min	Max
1	Saybolt fural viscosity @ 25?C sec	ASTM D224	—	25
2	Storage Stability (24 hours) %	ASTM D224	—	1
3	Sieve Test (%)	ASTM D224	—	0.1
4	Particle Charge Test	ASTM D224	Positive	—
5	Solubility in Trichloroethylene (% Mass)	ASTM D2042	97.5	—
6	Residue from distillation	ASTM D224	37	—
7	Penetration @ 25?C, 100g, 5sec	ASTM D5	60	200

Manufacturer of Iran Bitumen Emulsion K1-60

Technical Data Sheet of Cationic Bitumen Emulsion K1-60

No	Property	Result
1	Particle charge	Pos.
2	Residue on 710 um KS sieve (%)(m/m), maximum	0.05
3	Residue on 150 um KS sieve (g per 100 mL), maximum	0.15
4	Binder content (%)(m/m), minimum	57
5	Viscosity (degrees Engler (°E) at 20°C	6-9
6	Viscosity redwood No. II (s at 85°C)	–
7	Storage stability (long period test) % water content difference, maximum	2

High quality of Iran Cationic Bitumen Emulsion K1-70

Technical Data Sheet of Cationic Bitumen Emulsion K1-70

No	Property	Result
1	Particle charge	Pos.
2	Residue on 710 um KS sieve (%)(m/m), maximum	—
3	Residue on 150 um KS sieve (g per 100 mL), maximum	—
4	Binder content (%)(m/m), minimum	67
5	Viscosity (degrees Engler (°E) at 20°C	—
6	Viscosity redwood No. II (s at 85°C)	25-35
7	Storage stability (long period test) % water content difference, maximum	—

Iran Cationic Bitumen Emulsion K2 Producer

Technical Data Sheet of Cationic Bitumen Emulsion K2

No	Property	Result
1	Particle charge	Pos.
2	Residue on 710 um KS sieve (%)(m/m), maximum	0.05
3	Residue on 150 um KS sieve (g per 100 mL), maximum	0.15
4	Binder content (%)(m/m), minimum	57
5	Viscosity (degrees Engler (°E) at 20°C	10 max
6	Viscosity redwood No. II (s at 85°C)	–
7	Storage stability (long period test) % water content difference, maximum	2

Producer of High Quality Iran Cationc Bitumen Emulsion K3

Technical Data Sheet of Cationic Bitumen Emulsion K3

No	Property	Result
1	Particle charge	Pos.
2	Residue on 710 um KS sieve (%)(m/m), maximum	0.05
3	Residue on 150 um KS sieve (g per 100 mL), maximum	0.15
4	Binder content (%)(m/m), minimum	57
5	Viscosity (degrees Engler (°E) at 20°C	10 max
6	Viscosity redwood No. II (s at 85°C)	–
7	Storage stability (long period test) % water content difference, maximum	2

Cutback Bitumen

Cutback bitumen is a range of binders that are produced by blending (mixing) penetration grade bitumen and a hydrocarbon solvent, such as paraffin or mineral turpentine.

When the solvent has evaporated, the binder returns to its original penetration grade to tie the particles together. Cutback bitumen gets its name from the solvent that is involved in the process, because the solvent "cuts back" or evaporates, leaving behind the binder to "get on with the job". The solvent used in cutback bitumen is called the "cutter" or "flux".

Three types of solvents are used for the blending process: slow-curing, medium-curing or rapid-curing solvents. The latter two are the most common in South Africa. The choice of the solvent determines the rate at which the bitumen will cure when exposed to air. A rapid-curing (RC) solvent will evaporate faster than a medium-curing (MC) solvent. Curing relates to the evaporation rate of the solvent which influences the setting time of the bitumen. The viscosity of the cutback bitumen is determined by the proportion of solvent added: the higher the proportion of solvent, the lower the viscosity of the cutback.

Cutbacks differ from penetration grade bitumen in that they are more workable — in other words, they can be more easily reshaped. Less heat is required to liquefy cutback bitumen than penetration bitumen, making it easier to use at lower temperatures.

Typical cutback bitumens are MC 30 and RC 250. The letters in the name refer to the curing action of the solvent, and the number to the viscosity of the binder.

Specifications

cutback bitumen RC-30

guarantees that the Rapid curing CutBack Grade RC-30 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	30	60	ASTM D2170
Flashpoint(tag open cup), °c	—	—	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°f(360°c)
to 437°f(225°c) To 500°f(260°c) to 600°f(316°c) Residue from distillation to 680°f(360°c), percent volume by difference	55	—	ASTM D402
	75	—
	90	—
	50	—
Test on Residue from distillation test
Penetration 77°f(25°c) 100g,5s mm	80	120	ASTM D5
Ductility 77°f(25°c) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen RC-70

guarantees that the Rapid curing Cut Back Grade RC-70 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	70	140	ASTM D2170
Flash point(tag open cup), °c	—	—	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°f(360°c)
to 437°f(225°c) To 500°f(260°c) to 600°f(316°c) Residue from distillation to 680°f(360°c), percent volume by difference	50	—	ASTM D402
	70	—
	85	—
	55
Test on Residue from distillation test
Penetration 77°f(25°c) 100g,5s mm	80	120	ASTM D5
Ductility 77°f(25°c) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen RC-250

guarantees that the Rapid curing CutBack Grade RC-250 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028–97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	250	500	ASTM D2170
Flashpoint(tag open cup), °c	—	27	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°f (360°c)
to 437°f(225°c) To 500°f(260°c) to 600°f(316°c) Residue from distillation to 680°f(360°c), percent volume by difference	35	—	ASTM D402
	60	—
	80	—
	65	—
Test on Residue from distillation test
Penetration 77°f(25°c) 100g,5s mm	80	120	ASTM D5
Ductility 77°f(25°c) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen RC-800

guarantees that the Rapid curing CutBack Grade RC-800 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	800	1600	ASTM D2170
Flashpoint(tag open cup), °c	27	—	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°f (360°c)
to 437°f(225°c) To 500°f(260°c) to 600°f(316°c) Residue from distillation to 680°f(360°c), percent volume by difference	15	—	ASTM D402
	45	—
	75	—
	75	—
Test on Residue from distillation test
Penetration 77°f(25°c) 100g,5s mm	80	120	ASTM D5
Ductility 77°f(25°c) 5cm/min cm	100		ASTM D113
Solubility in trichloroethylene %	99		ASTM D2042
Water, percent volume		0.2	ASTM D95

cutback bitumen RC-3000

guarantees that the Rapid curing CutBack Grade RC-3000 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	3000	6000	ASTM D2170
Flashpoint(tag open cup), °c	—	27	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°F(360°F)
to 437°f(225°c) To 500°f(260°c) to 600°f(316°c) Residue from distillation to 680°f(360°c), percent volume by difference	—	—	ASTM D402
	25	—
	70	—
	80	—
Test on Residue from distillation test
Penetration 77°f(25°c) 100g,5s mm	80	120	ASTM D5
Ductility 77°f(25°c) 5cm/min cm	100		ASTM D113
Solubility in trichloroethylene %	99		ASTM D2042
Water, percent volume		0.2	ASTM D95

cutback bitumen MC-30

guarantees that the Medium Curing CutBack Grade MC-30 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	30	60	ASTM D2170
Flash point(tag open cup), °C	38	—	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°F (360°C)
to 437°F (225°C) To 500°F (260°C) to 600°F (316°C) Residue from distillation to 680°F(360°C), percent volume by difference	—	25	ASTM D402
	30	75
	75	95
	50	—
Test on Residue from distillation test
Viscosity at 140°F (60°C)	30	120	ASTM D2170
Penetration 77°F (25°C) 100g,5s mm	120	300	ASTM D5
Ductility 77°F (25°C) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen MC-70

guarantees that the Medium Curing CutBack Grade MC-70 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°C ,cST	70	140	ASTM D2170
Flashpoint(tag open cup), °C	38	—	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°F (360°C)
to 437°F (225°C) to 500°F (260°C) to 600°F (316°C) Residue from distillation to 680°F (360°C), percent volume by difference	—	20	ASTM D402
	10	70
	65	93
	55	—
Test on Residue from distillation test
Viscosity at 140°F (60°C)	30	120	ASTM D2170
Penetration 77°F (25°C) 100g,5s mm	120	300	ASTM D5
Ductility 77°F (25°C) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen MC-250

guarantees that the Medium Curing CutBack Grade MC-250 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	250	500	ASTM D2170
Flashpoint (tag open cup), °C	66	—	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°F (360°C)
to 437°F (225°C) To 500°F (260°C) to 600°F (316°C) Residue from distillation to 680°F (360°C), percent volume by difference	—	20	ASTM D402
	5	55
	60	90
	67	—
Test on Residue from distillation test
Viscosity at 140°f(60°C)	30	120	ASTM D2170
Penetration 77°F (25°C) 100g,5s mm	120	300	ASTM D5
Ductility 77°F (25°C) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen MC-800

guarantees that the Medium Curing CutBack Grade MC-800 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028–97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°C ,cST	800	1600	ASTM D2170
Flashpoint(tag open cup), °C	66		ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°F (360°C)
to 437°F (225°C) To 500°F (260°C) to 600°F (316°C) Residue from distillation to 680°F (360°C), percent volume by difference	—	—	ASTM D402
	—	40
	45	85
	75	—
Test on Residue from distillation test
Viscosity at 140°F (60°C)	30	120	ASTM D2170
Penetration 77°F (25°C) 100g,5s mm	120	250	ASTM D5
Ductility 77°F (25°C) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen MC-3000

guarantees that the Medium Curing CutBack Grade MC-3000 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°c ,cST	3000	6000	ASTM D2170
Flashpoint(tag open cup), °c	66	—	ASTM D3143
Distillation test Distillate, volume percent of total Distillate to 680°F (360°C)
to 437°F (225°C) to 500°F (260°C) to 600°F (316°C) Residue from distillation to 680°F (360°C), percent volume by difference	—	—	ASTM D402
	—	15
	15	75
	80	—
Test on Residue from distillation test
Viscosity at 140°F (60°C)	30	120	ASTM D2170
Penetration 77°F (25°C) 100g,5s mm	120	300	ASTM D5
Ductility 77°F (25°C) 5cm/min cm	100	—	ASTM D113
Solubility in trichloroethylene %	99	—	ASTM D2042
Water, percent volume	—	0.2	ASTM D95

cutback bitumen SC-70

guaranty the quality of cutback SC-70 with the arrangement of the international inspectors to check quality and quantity of the bitumen on each shipment during the loading to vessel and controlling the production by QC team via batch test report before shipping. RABIT guaranty the quality to meet with ASTM/EN 15322:2009

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°C [140°F], mm2/s	70	140	ASTM D2170
Flashpoint(Cleveland open cup), °C [°F]	60	—	ASTM D92
distillate test
Total distillate to 360°C [680°F], volume %	—	35	ASTM D402
Solubility, %	95	—	ASTM D2024
Kinematic viscosity on distillation residue at 60°C [140°F], mm2/s	200	7000	ASTM D2170
Asphalt residue:
Residue of 100 penetration, %	40	—	ASTM D243
Ductility of 100 penetration residue at 25°C [77°F], cm	50	—	ASTM D113
Water, %	—	0.5	ASTM D95

cutback bitumen SC-250

. guaranty the quality of cutback SC-250 with the arrangement of the international inspectors to check quality and quantity of the bitumen on each shipment during the loading to vessel and controlling the production by QC team via batch test report before shipping. RABIT guaranty the quality to meet with ASTM/EN 15322:2009.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°C [140°F], mm2/s	250	500	ASTM D2170
Flashpoint(Cleveland open cup), °C [°F]	60	—	ASTM D92
distillate test
Total distillate to 360°C [680°F], volume %	—	25	ASTM D402
Solubility, %	95	—	ASTM D2024
Kinematic viscosity on distillation residue at 60°C [140°F], mm2/s	400	10000	ASTM D2170
Asphalt residue:
Residue of 100 penetration, %	50	—	ASTM D243
Ductility of 100 penetration residue at 25°C [77°F], cm	50	—	ASTM D113
Water, %	—	0.5	ASTM D95

cutback bitumen SC-800

guaranty the quality of cutback SC-800 with the arrangement of the international inspectors to check quality and quantity of the bitumen on each shipment during the loading to vessel and controlling the production by QC team via batch test report before shipping. RABIT guaranty the quality to meet with ASTM/EN 15322:2009.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°C [140°F], mm2/s	800	1600	ASTM D2170
Flashpoint(Cleveland open cup), °C [°F]	70	—	ASTM D92
distillate test
Total distillate to 360°C [680°F], volume %	—	15	ASTM D402
Solubility, %	95	—	ASTM D2024
Kinematic viscosity on distillation residue at 60°C [140°F], mm2/s	1000	16000	ASTM D2170
Asphalt residue:
Residue of 100 penetration, %	60	—	ASTM D243
Ductility of 100 penetration residue at 25°C [77°F], cm	50	—	ASTM D113
Water, %	—	0.5	ASTM D95

cutback bitumen SC-3000

guaranty the quality of cutback SC-3000 with the arrangement of the international inspectors to check quality and quantity of the bitumen on each shipment during the loading to vessel and controlling the production by QC team via batch test report before shipping. RABIT guaranty the quality to meet with ASTM/EN 15322:2009.

property	specification limit		Test method
property	Min	Max	Test method
Kinematic viscosity at 60°C [140°F], mm2/s	3000	6000	ASTM D2170
Flashpoint(Cleveland open cup), °C [°F]	70	—	ASTM D92
distillate test
Total distillate to 360°C [680°F], volume %	—	8	ASTM D402
Solubility, %	95	—	ASTM D2024
Kinematic viscosity on distillation residue at 60°C [140°F], mm2/s	2000	35000	ASTM D2170
Asphalt residue:
Residue of 100 penetration, %	75	—	ASTM D243
Ductility of 100 penetration residue at 25°C [77°F], cm	50	—	ASTM D113
Water, %	—	0.5	ASTM D95

Bitumen Coating

Bitumen coating compositions having substantially improved application and drying properties and producing coatings of improved properties including resistance to ultraviolet rays and alligatoring resulting therefrom said coating compositions comprising volatile solvent solutions of a bitumen coating material having softening point between 110 F To 250 F. The bitumen coating are also characteristically non-viscous materials which are not thixotropic and are therefore ordinarily applied as thin films. The bitumen coating compositions may also contain filler materials which tend to settle from the non-thixotropic compositions after storage for only a short time. It has been proposed in the past to add inert colloidal fillers such as silica to obtain thixotropic properties and thicker films on the application of the compositions. However, even such inert fillers tend to affect only solution properties and generally exist in the finished coating as an expensive additive which does not benefit other properties of the coating.

Specifications

GT550 Outer-Wrap

Technical Data of GT550 Outer-wrap

Properties	Unit	Requirement	Method of test
Mass per area of base glass/carrier	gr /m2	Min 80	EN 10300, Annex M
Type of base glass/carrier	—	Non-woven glass fibre tissue	—
Mass per area	gr /m2	Min 550	EN 10300, Annex M
Thickness	mm	Min 0.76	EN 1849-1a
Tensile Strength – Longitudinal – Transverse N	N/50mm N/50mm	Min 300 Min 230	EN 12311-1 modified as in Annex N of EN 10300

Iso Polymer Bitumen

Specification of Iso Polymer Bitumen

Softening Point	90-95°C
Elongation	Over 400%
Flash Point	Over 250°C